Acrylic and Chlo... B52-2 Acrylic Mastic Finish Coating

1. Based on acrylic resin, plasticiser, thixotropic agent, filler, pigment and solvent.
2. Physical dryness type.
3. Excellent stand wear and tear ability and crashworthiness.
4. Excellent resistance to sea water, mineral oil and other propagation oil.
5. The luster is half glossy with excellent color retention.
6. Thick film. Can reduce layers.   

Recommended uses

1. Suitable as the finish coating for contianer and project mechines. As anticossosion finish coating for other steel structure and concrete.

Physical parameter

Color

All color

Theoretic coverage

300g/

Specific gravity

About 1.20

Desiccation time

23±2surface dryness≤4 h, Actual dryness≤ 8h

Flash point

25 ℃

Storage

8 months

Operation description

Mixing ratio

Single canned

Curing time

Using after minxing up

Applicable time

Limitless

Thinner

X-14 Chlorinated rubber coating thinner

Operation method

Airless spraying

Air spraying

Manual brushing /Roller coat

Max capacity of dilution

5%

10%

3%

Spout size

0.4-0.5mm

2.0-2.5mm

-

Spray pressure

15-20Mpa

0.3-0.5Mpa

-

Tool cleaning

X-14 Chlorinated rubber coating thinner

Film thickness

Wet film: 200 um        Dry film: 75 um

Operation interval

Temperature of the base

0℃

20℃

30℃

Min.

24 hours

8 hours

6 hours

Max.

Limitless

Surface treatment

1. If the foregoing paint has been polluted, clear the oil, dust by correct way or using the thinner. 

Operation condition

1. Temperature of the base material should 3℃ higher than the dew point and the RH should below 85%.

Foregoing